Data Table for:Ti Alloy:Titanium 1100 Ti Alloy

Steel grade type Ti Alloy:
Standard
Production specifications Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
Mchining Turning
Milling
Grinding
Deep hole drilling: length max 9.8 meters.
Range of work

Round bar steel: 1mm to 2000mm

Square-shape steel: 10mm to 1000mm

steel Plate/sheet:0.08mm to 800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.

Heat treatment Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing

Titanium 1100 Ti Alloy Chemical composition and Mechanical properties

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTitanium 1100 plate,Titanium 1100 Round Bar,Titanium 1100 forgings,Titanium 1100 suppliers, Titanium 1100 Stock,Titanium 1100 sheet, Titanium 1100 flat bar, Titanium 1100 pipe,Titanium 1100 tube,Titanium 1100 mould,Titanium 1100 round ingot,Titanium 1100 cold-rolled steel,Titanium 1100 coil,Titanium 1100 strap steel,Titanium 1100 hot-rolled steel,Titanium 1100 medium plate, Titanium 1100 heavy plate,Titanium 1100 shapped bar,Titanium 1100 hexahedral bar,Titanium 1100,Titanium 1100 slab ingot,Titanium 1100 slab,Titanium 1100 price,Titanium 1100 square bar,Titanium 1100 square steel,Titanium 1100 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Titanium 1100.

 

Titanium 1100 Ti Alloy

Our advantages

Titanium 1100 properties and heat treatment forged piece, Including Titanium 1100 application and specifications, We have all specifications,Including Titanium 1100 steel plate, Titanium 1100 sheet, Titanium 1100 square steel, Titanium 1100 flat bar,Titanium 1100 round bar,Titanium 1100 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Titanium 1100 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Titanium 1100 and Standards

Titanium 1100 Beta Quenched and annealed
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes:

Key Words: Titanium 1100

 

Physical Properties Metric English Comments
Density 4.50 g/cc 0.163 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1010 MPa 146000 psi
  750 MPa
@Temperature 400 °C
109000 psi
@Temperature 752 °F
Tensile Strength, Yield 910 MPa 132000 psi
  625 MPa
@Temperature 400 °C
90600 psi
@Temperature 752 °F
Elongation at Break 11.0 % 11.0 %
Modulus of Elasticity 107 - 117 GPa 15500 - 17000 ksi
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Fatigue Strength 250 MPa
@# of Cycles 1.00e+7
36300 psi
@# of Cycles 1.00e+7
notched with Kt = 3.0.
  655 MPa
@# of Cycles 1.00e+7
95000 psi
@# of Cycles 1.00e+7
notched with Kt = 1.0.
Fracture Toughness 63.0 MPa-m½ 57.3 ksi-in½ K(IC) after 1095ºC anneal
Shear Modulus 42.7 GPa 6190 ksi Calculated from typical values.
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm Estimated from similar alpha titanium alloys.
 
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C
@Temperature 20.0 - 100 °C
5.00 µin/in-°F
@Temperature 68.0 - 212 °F
Typical alpha titanium alloy
Specific Heat Capacity 0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity 7.00 W/m-K 48.6 BTU-in/hr-ft²-°F Estimated from similar titanium alloys.
Beta Transus 1015 °C 1859 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 6.0 % 6.0 %
Molybdenum, Mo 0.40 % 0.40 %
Silicon, Si 0.40 % 0.40 %
Tin, Sn 2.70 % 2.70 %
Titanium, Ti 87.0 % 87.0 %
Zirconium, Zr 4.0 % 4.0 %

 

Users viewing this material also viewed the following:
Aluminum 6061-T6; 6061-T651
AISI 4140 Steel, normalized at 870°C (1600°F), air cooled, 100 mm (4 in.) round
Titanium, Ti
Allegheny Ludlum Grade 1 Titanium (UNS R50250)
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed

MTA993 / 14143




Machining performance

Download Titanium 1100 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Titanium 1100 steel plate, Titanium 1100 sheet, Titanium 1100 square steel, Titanium 1100 flat bar,Titanium 1100 round bar,Titanium 1100 forgings

 
 

关闭提示 关闭

 

确 认 取 消

Mechanical Properties

Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1158 25 oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa) 1034
Elongation (%) 15
Reduction in Area (%) 53
Hardness (HB) 335 25 oil quenched, fine grained, tempered at 425°C

Thermal Properties

Properties Conditions
T (°C) Treatment
Thermal Conductivity (W/m-K) 42.7 100  
Specific Heat (J/kg-K) 477 50-100  
Physical Properties
Quantity Value Unit
Thermal expansion 16 - 17 e-6/K
Thermal conductivity 16 - 16 W/m.K
Specific heat 500 - 500 J/kg.K
Melting temperature 1370 - 1400 °C
Service temperature 0 - 500 °C
Density 8000 - 8000 kg/m3
Resistivity 0.7 - 0.7 Ohm.mm2/m