UNS R58030 Ti Alloy

Data Table for:Ti Alloy:UNS R58030 Ti Alloy

Steel grade type Ti Alloy:
Production specifications Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
Mchining Turning
Deep hole drilling: length max 9.8 meters.
Range of work

Round bar steel: 1mm to 2000mm

Square-shape steel: 10mm to 1000mm

steel Plate/sheet:0.08mm to 800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.

Heat treatment Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing

UNS R58030 Ti Alloy Chemical composition and Mechanical properties


Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyUNS R58030 plate,UNS R58030 Round Bar,UNS R58030 forgings,UNS R58030 suppliers, UNS R58030 Stock,UNS R58030 sheet, UNS R58030 flat bar, UNS R58030 pipe,UNS R58030 tube,UNS R58030 mould,UNS R58030 round ingot,UNS R58030 cold-rolled steel,UNS R58030 coil,UNS R58030 strap steel,UNS R58030 hot-rolled steel,UNS R58030 medium plate, UNS R58030 heavy plate,UNS R58030 shapped bar,UNS R58030 hexahedral bar,UNS R58030,UNS R58030 slab ingot,UNS R58030 slab,UNS R58030 price,UNS R58030 square bar,UNS R58030 square steel,UNS R58030 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS R58030.


UNS R58030 Ti Alloy

Our advantages

UNS R58030 properties and heat treatment forged piece, Including UNS R58030 application and specifications, We have all specifications,Including UNS R58030 steel plate, UNS R58030 sheet, UNS R58030 square steel, UNS R58030 flat bar,UNS R58030 round bar,UNS R58030 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the UNS R58030 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade UNS R58030 and Standards

Titanium Beta III (Ti-11.5Mo-6Zr-4.5Sn; Grade 10), Solution Treated, Unaged
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Material Notes: 5 other heat treatments of this alloy are in MatWeb.

Key Words: Ti-11.5Mo-6Zr-4.5Sn; UNS R58030; Beta 3


Physical Properties Metric English Comments
Density 5.06 g/cc 0.183 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers 240 240
Tensile Strength, Ultimate 725 MPa 105000 psi
Tensile Strength, Yield 620 MPa 89900 psi
Elongation at Break 15.0 % 15.0 %
Reduction of Area 65.0 % 65.0 %
Modulus of Elasticity 79.0 GPa 11500 ksi
Compressive Yield Strength 800 MPa 116000 psi
Poissons Ratio 0.360 0.360
Fracture Toughness 160 MPa-m½ 146 ksi-in½ K(IC)
Shear Modulus 27.0 GPa 3920 ksi
Shear Strength 590 MPa 85600 psi Ultimate shear strength
Electrical Properties Metric English Comments
Electrical Resistivity 0.000156 ohm-cm 0.000156 ohm-cm
Thermal Properties Metric English Comments
CTE, linear 7.60 µm/m-°C
@Temperature 20.0 - 100 °C
4.22 µin/in-°F
@Temperature 68.0 - 212 °F
  8.10 µm/m-°C
@Temperature 20.0 - 315 °C
4.50 µin/in-°F
@Temperature 68.0 - 599 °F
  8.70 µm/m-°C
@Temperature 20.0 - 540 °C
4.83 µin/in-°F
@Temperature 68.0 - 1000 °F
Specific Heat Capacity 0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity 6.28 W/m-K 43.6 BTU-in/hr-ft²-°F
Melting Point 1573 - 1690 °C 2863 - 3070 °F
Solidus 1573 °C 2863 °F
Liquidus 1690 °C 3070 °F
Beta Transus 760 °C 1400 °F Slow transition kinetics
Component Elements Properties Metric English Comments
Molybdenum, Mo 11.5 % 11.5 %
Tin, Sn 4.50 % 4.50 %
Titanium, Ti 78.0 % 78.0 %
Zirconium, Zr 6.0 % 6.0 %


Users viewing this material also viewed the following:
Titanium Beta III (Ti-11.5Mo-6Zr-4.5Sn; Grade 10), ST 720°C, Aged 550°C
Titanium Ti-3Al-2.5V (Grade 9), Alpha-Beta Anneal, Quenched
Titanium Ti-11.5Mo-6Zr-4.5Sn, ST 720°C, Aged 495°C
Titanium Beta C (Ti-3Al-8V-6Cr-4Mo-4Zr) Solution Treated 815°C
Titanium Ti-5-5-2-3 (Ti-5Mo-5V-2Cr-3Al), 12 mm Rod, Aged

MTB030 / 14152

Machining performance

Download UNS R58030 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:UNS R58030 steel plate, UNS R58030 sheet, UNS R58030 square steel, UNS R58030 flat bar,UNS R58030 round bar,UNS R58030 forgings


关闭提示 关闭


确 认 取 消

Mechanical Properties

Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1158 25 oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa) 1034
Elongation (%) 15
Reduction in Area (%) 53
Hardness (HB) 335 25 oil quenched, fine grained, tempered at 425°C

Thermal Properties

Properties Conditions
T (°C) Treatment
Thermal Conductivity (W/m-K) 42.7 100  
Specific Heat (J/kg-K) 477 50-100  
Physical Properties
Quantity Value Unit
Thermal expansion 16 - 17 e-6/K
Thermal conductivity 16 - 16 W/m.K
Specific heat 500 - 500 J/kg.K
Melting temperature 1370 - 1400 °C
Service temperature 0 - 500 °C
Density 8000 - 8000 kg/m3
Resistivity 0.7 - 0.7 Ohm.mm2/m