Ti8Al1Mo1V Ti Alloy

Data Table for:Ti Alloy:Ti8Al1Mo1V Ti Alloy

Steel grade type Ti Alloy:
Standard
Production specifications Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
Mchining Turning
Milling
Grinding
Deep hole drilling: length max 9.8 meters.
Range of work

Round bar steel: 1mm to 2000mm

Square-shape steel: 10mm to 1000mm

steel Plate/sheet:0.08mm to 800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.

Heat treatment Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing

Ti8Al1Mo1V Ti Alloy Chemical composition and Mechanical properties

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi8Al1Mo1V plate,Ti8Al1Mo1V Round Bar,Ti8Al1Mo1V forgings,Ti8Al1Mo1V suppliers, Ti8Al1Mo1V Stock,Ti8Al1Mo1V sheet, Ti8Al1Mo1V flat bar, Ti8Al1Mo1V pipe,Ti8Al1Mo1V tube,Ti8Al1Mo1V mould,Ti8Al1Mo1V round ingot,Ti8Al1Mo1V cold-rolled steel,Ti8Al1Mo1V coil,Ti8Al1Mo1V strap steel,Ti8Al1Mo1V hot-rolled steel,Ti8Al1Mo1V medium plate, Ti8Al1Mo1V heavy plate,Ti8Al1Mo1V shapped bar,Ti8Al1Mo1V hexahedral bar,Ti8Al1Mo1V,Ti8Al1Mo1V slab ingot,Ti8Al1Mo1V slab,Ti8Al1Mo1V price,Ti8Al1Mo1V square bar,Ti8Al1Mo1V square steel,Ti8Al1Mo1V wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti8Al1Mo1V.

 

Ti8Al1Mo1V Ti Alloy

Our advantages

Ti8Al1Mo1V properties and heat treatment forged piece, Including Ti8Al1Mo1V application and specifications, We have all specifications,Including Ti8Al1Mo1V steel plate, Ti8Al1Mo1V sheet, Ti8Al1Mo1V square steel, Ti8Al1Mo1V flat bar,Ti8Al1Mo1V round bar,Ti8Al1Mo1V forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti8Al1Mo1V has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti8Al1Mo1V and Standards

Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), Beta Annealed, Aged
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes: Information provided by Allvac and the references. Annealed at 1065ºC, Aged at 595ºC.

Applications: Fan & compressor blades, discs, spacers, seals, rings. Excellent creep resistance.

5 other heat treatments of this alloy are in MatWeb.

Key Words: Ti8Al1Mo1V, UNS R54810; Ti-811

 

Physical Properties Metric English Comments
Density 4.37 g/cc 0.158 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1020 MPa 148000 psi
Tensile Strength, Yield 900 MPa 131000 psi
Elongation at Break 13.0 % 13.0 %
Modulus of Elasticity 120 GPa 17400 ksi unspecified heat treatment
Poissons Ratio 0.320 0.320 duplex annealed
Shear Modulus 46.0 GPa 6670 ksi
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000197 ohm-cm 0.000197 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 8.50 µm/m-°C
@Temperature 20.0 °C
4.72 µin/in-°F
@Temperature 68.0 °F
  9.20 µm/m-°C
@Temperature 250 °C
5.11 µin/in-°F
@Temperature 482 °F
  10.1 µm/m-°C
@Temperature 500 °C
5.61 µin/in-°F
@Temperature 932 °F
Specific Heat Capacity 0.502 J/g-°C 0.120 BTU/lb-°F
Thermal Conductivity 6.00 W/m-K 41.6 BTU-in/hr-ft²-°F
Melting Point <= 1540 °C <= 2800 °F Liquidus
Liquidus 1540 °C 2800 °F
Beta Transus 1040 °C 1900 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 7.35 - 8.35 % 7.35 - 8.35 %
Carbon, C <= 0.0800 % <= 0.0800 %
Hydrogen, H <= 0.0150 % <= 0.0150 %
Iron, Fe <= 0.300 % <= 0.300 %
Molybdenum, Mo 0.750 - 1.25 % 0.750 - 1.25 %
Nitrogen, N <= 0.0500 % <= 0.0500 %
Other, each <= 0.100 % <= 0.100 %
Other, total <= 0.400 % <= 0.400 %
Oxygen, O <= 0.120 % <= 0.120 %
Titanium, Ti 88.185 - 91.15 % 88.185 - 91.15 % As Balance; Elemental Compostions per ASTM B265
Vanadium, V 0.750 - 1.25 % 0.750 - 1.25 %

 

Users viewing this material also viewed the following:
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), ST 980°C (1800°F), Aged 595°C
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1)
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), Beta Solution Treated
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1) Duplex Anneal
Titanium Ti-6Al-4V (Grade 5), Annealed

MTA811 / 14136




Machining performance

Download Ti8Al1Mo1V the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti8Al1Mo1V steel plate, Ti8Al1Mo1V sheet, Ti8Al1Mo1V square steel, Ti8Al1Mo1V flat bar,Ti8Al1Mo1V round bar,Ti8Al1Mo1V forgings

 
 

关闭提示 关闭

 

确 认 取 消

Mechanical Properties

Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1158 25 oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa) 1034
Elongation (%) 15
Reduction in Area (%) 53
Hardness (HB) 335 25 oil quenched, fine grained, tempered at 425°C

Thermal Properties

Properties Conditions
T (°C) Treatment
Thermal Conductivity (W/m-K) 42.7 100  
Specific Heat (J/kg-K) 477 50-100  
Physical Properties
Quantity Value Unit
Thermal expansion 16 - 17 e-6/K
Thermal conductivity 16 - 16 W/m.K
Specific heat 500 - 500 J/kg.K
Melting temperature 1370 - 1400 °C
Service temperature 0 - 500 °C
Density 8000 - 8000 kg/m3
Resistivity 0.7 - 0.7 Ohm.mm2/m