Ti15Mo5Zr3Al Ti Alloy

Data Table for:Ti Alloy:Ti15Mo5Zr3Al Ti Alloy

Steel grade type Ti Alloy:
Standard
Production specifications Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
Mchining Turning
Milling
Grinding
Deep hole drilling: length max 9.8 meters.
Range of work

Round bar steel: 1mm to 2000mm

Square-shape steel: 10mm to 1000mm

steel Plate/sheet:0.08mm to 800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.

Heat treatment Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing

Ti15Mo5Zr3Al Ti Alloy Chemical composition and Mechanical properties

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi15Mo5Zr3Al plate,Ti15Mo5Zr3Al Round Bar,Ti15Mo5Zr3Al forgings,Ti15Mo5Zr3Al suppliers, Ti15Mo5Zr3Al Stock,Ti15Mo5Zr3Al sheet, Ti15Mo5Zr3Al flat bar, Ti15Mo5Zr3Al pipe,Ti15Mo5Zr3Al tube,Ti15Mo5Zr3Al mould,Ti15Mo5Zr3Al round ingot,Ti15Mo5Zr3Al cold-rolled steel,Ti15Mo5Zr3Al coil,Ti15Mo5Zr3Al strap steel,Ti15Mo5Zr3Al hot-rolled steel,Ti15Mo5Zr3Al medium plate, Ti15Mo5Zr3Al heavy plate,Ti15Mo5Zr3Al shapped bar,Ti15Mo5Zr3Al hexahedral bar,Ti15Mo5Zr3Al,Ti15Mo5Zr3Al slab ingot,Ti15Mo5Zr3Al slab,Ti15Mo5Zr3Al price,Ti15Mo5Zr3Al square bar,Ti15Mo5Zr3Al square steel,Ti15Mo5Zr3Al wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti15Mo5Zr3Al.

Ti15Mo5Zr3Al Ti Alloy

Our advantages

Ti15Mo5Zr3Al properties and heat treatment forged piece, Including Ti15Mo5Zr3Al application and specifications, We have all specifications,Including Ti15Mo5Zr3Al steel plate, Ti15Mo5Zr3Al sheet, Ti15Mo5Zr3Al square steel, Ti15Mo5Zr3Al flat bar,Ti15Mo5Zr3Al round bar,Ti15Mo5Zr3Al forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti15Mo5Zr3Al has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti15Mo5Zr3Al and Standards

Ti15Mo5Zr3Al ß titanium alloy
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Key Words: medical, surgical

 

Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 882 MPa 128000 psi solution heat treatment at 840°C
  882 - 1177 MPa 128000 - 170700 psi as forged and aged (600°C)
  1099 MPa 159400 psi solution heat treatment at 740°C + aged at 600°C
Tensile Strength, Yield 870 MPa 126000 psi 0.2%, solution heat treatment at 840°C
  870 - 1173 MPa 126000 - 170100 psi as forged and aged (600°C)
  1087 MPa 157700 psi 0.2%, solution heat treatment at 740°C + aged at 600°C
Elongation at Break 15.3 % 15.3 % solution heat treatment at 740°C + aged at 600°C
  15.0 - 20.0 % 15.0 - 20.0 % as forged and aged (600°C)
  20.0 % 20.0 % solution heat treatment at 840°C
Reduction of Area 57.5 % 57.5 % solution heat treatment at 740°C + aged at 600°C
  43.0 - 80.0 % 43.0 - 80.0 % as forged and aged (600°C)
  83.2 % 83.2 % solution heat treatment at 840°C
Modulus of Elasticity 75.0 GPa 10900 ksi Solution heat treated at 840°C
  88.0 GPa 12800 ksi Solution heat treated at 740°C
  113 GPa 16400 ksi Solution heat treated at 740°C + aged at 600°C
 
Component Elements Properties Metric English Comments
Aluminum, Al 3.80 % 3.80 %
Molybdenum, Mo 15.0 % 15.0 %
Titanium, Ti 76.2 % 76.2 %
Zirconium, Zr 5.0 % 5.0 %

 

Users viewing this material also viewed the following:
Titanium, Ti
Ti30Nb ß titanium alloy
Overview of materials for Beta Titanium Alloy
Ti6Al7Nb ASTM F1295
Ti30Ta ß titanium alloy

MMEDIC26 / 12402




Machining performance

Download Ti15Mo5Zr3Al the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti15Mo5Zr3Al steel plate, Ti15Mo5Zr3Al sheet, Ti15Mo5Zr3Al square steel, Ti15Mo5Zr3Al flat bar,Ti15Mo5Zr3Al round bar,Ti15Mo5Zr3Al forgings

 
 

关闭提示 关闭

 

确 认 取 消

Mechanical Properties

Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1158 25 oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa) 1034
Elongation (%) 15
Reduction in Area (%) 53
Hardness (HB) 335 25 oil quenched, fine grained, tempered at 425°C

Thermal Properties

Properties Conditions
T (°C) Treatment
Thermal Conductivity (W/m-K) 42.7 100  
Specific Heat (J/kg-K) 477 50-100  
Physical Properties
Quantity Value Unit
Thermal expansion 16 - 17 e-6/K
Thermal conductivity 16 - 16 W/m.K
Specific heat 500 - 500 J/kg.K
Melting temperature 1370 - 1400 °C
Service temperature 0 - 500 °C
Density 8000 - 8000 kg/m3
Resistivity 0.7 - 0.7 Ohm.mm2/m