Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si Ti Alloy

Data Table for:Ti Alloy:Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si Ti Alloy

Steel grade type Ti Alloy:
Standard
Production specifications Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
Mchining Turning
Milling
Grinding
Deep hole drilling: length max 9.8 meters.
Range of work

Round bar steel: 1mm to 2000mm

Square-shape steel: 10mm to 1000mm

steel Plate/sheet:0.08mm to 800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.

Heat treatment Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing

Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si Ti Alloy Chemical composition and Mechanical properties

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-11Sn-5Zr-2.25Al-1Mo-0.25Si plate,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si Round Bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si forgings,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si suppliers, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si Stock,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si sheet, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si flat bar, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si pipe,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si tube,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si mould,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si round ingot,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si cold-rolled steel,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si coil,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si strap steel,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si hot-rolled steel,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si medium plate, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si heavy plate,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si shapped bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si hexahedral bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si slab ingot,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si slab,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si price,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si square bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si square steel,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si.

 

Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si Ti Alloy

Our advantages

Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si properties and heat treatment forged piece, Including Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si application and specifications, We have all specifications,Including Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si steel plate, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si sheet, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si square steel, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si flat bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si round bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si and Standards

Titanium IMI 679 (Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si), Oil-Quenched and Aged
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes: Alpha Prime Transus 880ºC. Tensile Properties below after oil quench/aged heat treatment: 900°C/OQ, 500°C/24hr/AC.

Key Words: Ti11Sn5Zr2.25Al1Mo0.25Si

 

Physical Properties Metric English Comments
Density 4.84 g/cc 0.175 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1110 MPa 161000 psi
Tensile Strength, Yield 970 MPa 141000 psi
Elongation at Break 8.00 % 8.00 %
Reduction of Area 25.0 % 25.0 %
Modulus of Elasticity 115 GPa 16700 ksi Typical value for an alpha titanium alloy
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Fatigue Strength 110 MPa
@# of Cycles 1.00e+7
16000 psi
@# of Cycles 1.00e+7
Kt = 3.0; R = -1.0 (air-cooled and aged sample)
  200 MPa
@# of Cycles 50000
29000 psi
@# of Cycles 50000
Kt = 3.0; R = -1.0 (air-cooled and aged sample)
  390 MPa
@# of Cycles 1.00e+7
56600 psi
@# of Cycles 1.00e+7
(air-cooled and aged sample)
  590 MPa
@# of Cycles 50000
85600 psi
@# of Cycles 50000
(air-cooled and aged sample)
Shear Modulus 43.9 GPa 6370 ksi Calculated from typical values.
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 8.60 µm/m-°C
@Temperature 20.0 °C
4.78 µin/in-°F
@Temperature 68.0 °F
  9.30 µm/m-°C
@Temperature 250 °C
5.17 µin/in-°F
@Temperature 482 °F
  10.0 µm/m-°C
@Temperature 500 °C
5.56 µin/in-°F
@Temperature 932 °F
Specific Heat Capacity 0.500 J/g-°C 0.120 BTU/lb-°F
Thermal Conductivity 8.30 W/m-K 57.6 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 450 °C 842 °F
Beta Transus 880 °C 1620 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 2.25 % 2.25 %
Molybdenum, Mo 1.0 % 1.0 %
Silicon, Si 0.25 % 0.25 %
Tin, Sn 11.0 % 11.0 %
Titanium, Ti 81.0 % 81.0 %
Zirconium, Zr 5.0 % 5.0 %

 

Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium Ti-8Al-1Mo-1V (Ti-8-1-1), ST 980°C (1800°F), Aged 595°C
Titanium Ti-6Al-2Nb-1Ta-1Mo
Titanium Ti-3Al-2.5V (Grade 9), Alpha-Beta Anneal, Quenched
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed

MTA670 / 14134




Machining performance

Download Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si steel plate, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si sheet, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si square steel, Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si flat bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si round bar,Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si forgings

 
 

关闭提示 关闭

 

确 认 取 消

Mechanical Properties

Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1158 25 oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa) 1034
Elongation (%) 15
Reduction in Area (%) 53
Hardness (HB) 335 25 oil quenched, fine grained, tempered at 425°C

Thermal Properties

Properties Conditions
T (°C) Treatment
Thermal Conductivity (W/m-K) 42.7 100  
Specific Heat (J/kg-K) 477 50-100  
Physical Properties
Quantity Value Unit
Thermal expansion 16 - 17 e-6/K
Thermal conductivity 16 - 16 W/m.K
Specific heat 500 - 500 J/kg.K
Melting temperature 1370 - 1400 °C
Service temperature 0 - 500 °C
Density 8000 - 8000 kg/m3
Resistivity 0.7 - 0.7 Ohm.mm2/m

Hot keywords:Ti-11Sn-5Zr-2.25Al-1Mo-0.25Si Ti

Previous page:IMI 679 Ti Alloy
Next pageTi11Sn5Zr2.25Al1Mo0.25Si Ti Alloy

Favorite