Current Location:Home >> Ti Alloy > 3.7235 Ti Alloy

3.7235 Ti Alloy

Data Table for:Ti Alloy:3.7235 Ti Alloy

Steel grade type Ti Alloy:
Standard
Production specifications Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
Mchining Turning
Milling
Grinding
Deep hole drilling: length max 9.8 meters.
Range of work

Round bar steel: 1mm to 2000mm

Square-shape steel: 10mm to 1000mm

steel Plate/sheet:0.08mm to 800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.

Heat treatment Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing

3.7235 Ti Alloy Chemical composition and Mechanical properties

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti Alloy3.7235 plate,3.7235 Round Bar,3.7235 forgings,3.7235 suppliers, 3.7235 Stock,3.7235 sheet, 3.7235 flat bar, 3.7235 pipe,3.7235 tube,3.7235 mould,3.7235 round ingot,3.7235 cold-rolled steel,3.7235 coil,3.7235 strap steel,3.7235 hot-rolled steel,3.7235 medium plate, 3.7235 heavy plate,3.7235 shapped bar,3.7235 hexahedral bar,3.7235,3.7235 slab ingot,3.7235 slab,3.7235 price,3.7235 square bar,3.7235 square steel,3.7235 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 3.7235.

Our advantages

3.7235 properties and heat treatment forged piece, Including 3.7235 application and specifications, We have all specifications,Including 3.7235 steel plate, 3.7235 sheet, 3.7235 square steel, 3.7235 flat bar,3.7235 round bar,3.7235 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 3.7235 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 3.7235 and Standards

3.7235




Machining performance

Download 3.7235 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:3.7235 steel plate, 3.7235 sheet, 3.7235 square steel, 3.7235 flat bar,3.7235 round bar,3.7235 forgings

Mechanical Properties

Properties Conditions
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 1158 25 oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa) 1034
Elongation (%) 15
Reduction in Area (%) 53
Hardness (HB) 335 25 oil quenched, fine grained, tempered at 425°C

Thermal Properties

Properties Conditions
T (°C) Treatment
Thermal Conductivity (W/m-K) 42.7 100  
Specific Heat (J/kg-K) 477 50-100  
Physical Properties
Quantity Value Unit
Thermal expansion 16 - 17 e-6/K
Thermal conductivity 16 - 16 W/m.K
Specific heat 500 - 500 J/kg.K
Melting temperature 1370 - 1400 °C
Service temperature 0 - 500 °C
Density 8000 - 8000 kg/m3
Resistivity 0.7 - 0.7 Ohm.mm2/m